Bearing malignant fever several solutions

A, bearing workpiece heat treatment of solid solution treatment is not suitable for high temperature, heat preservation time is not suitable for too long, the heating temperature should be no higher than 1150 'C, heat preservation time to 1 - It is advisable to l_5min/mm calculation. Lcrl8Ni9Ti with stainless steel body or flange when was overheating, lack of easy initiation of orange peel shape appearance. If the office is interrupted, should with oil paper plastic film or roughly similar material by machine. And then is to transform the bearing lubricating oil agent. Second, the strict restrict lcrl8Ni9] Ri stainless steel casing, flange forging heating temperature and heating heat preservation time, avoid overheating work revealed the workpiece initiation grain thick. Through the three steps can good good maintenance of your bearings, make its use fixed number of year of the survival of greatly increase, save your operating costs. After using oil lubricating oil bearing in xie used engine oil, if can of words, should the oil impregnated with novel and let the machine in low speed rotation for a few minutes. In regular outage protection aftercare change over a period of time than bearing because array bearing destroy selected into suddenly stop the loss of much more economical. It is possible to do oil residual pollutants, make together then have diarrhoea except the oil. Three, to prevent excessive groups of heavy work, can see fit and use to forge refine grain to eliminate, avoid the workpiece during cold deformation was lack of orange peel shape appearance, improve the appearance quality of the workpiece. Four,. Seizing the bearing lubricant agent seizing bearing don't let the bearing show in the background of the contaminants or moisture. Five, the workpiece in forging production, such as forging ratio is too small, the final forging temperature on the high side, also easy to appear coarse grain groups lack, should make workpiece forging ratio appropriate, sufficient, finish forging temperature is moderate. With a little mirror, and the probe used in the roughly similar to the dentist to seizing bearing orbit plane, sustain and beads.