Analysis: key bearing surface treatment technology - bearing knowledge

Main ingredients: high molecular polyester card borane polymer resin; Nanometer molybdenum disulfide; Rust and oil absorption nano groups; Micro ptfe nano powder mixture, etc. Above all raw materials developed by my small production and laboratory. Purpose: to improve bearing surface rust resistance; Reduce surface friction coefficient; Friction and wear resistant comprehensive performance. 3. Usage suggestion: 1) Remove the bearing surface of antirust oil, etc. 1. Press with research and development of our industrial efficient degreasing powder is mixed with water and 1% and 3%, the bearing ring into the fluid in the heat to 70 degrees to 85 degrees for 30 minutes ( Need to continuous stirring) , stop heating from cold to 40 degrees one bearing ring immersed in water brush with wool washing, especially of spherical bearing work to scrub a few times more, when scrubbing of bearing ring can't leave the water. Note: this fluid can float on the surface of the water to remove the oil bead after reuse again; 2. Use about 40 degrees to rinse it twice, the two rinse water in a reusable; The proportion of heavy oil with 3% and weighed more than with a cleaning fluid scrub twice; 2) Use LM - 1198 a type super concentrated cleaning fluid will dip phosphating within the deep layer of microporous lubricating oil removal, for generation such as molybdenum disulfide resin make position. The specific method of use according to 0. The proportion of 5% with water cleaner heat to 85 degrees to 99 degrees ( Drip down cleaning agent can pick up cold after removing oil floating on the surface after pearl reusable once) , bearing the workpiece immersion in cleaner with brush wash, and then rinse it twice with over 70 degrees temperature. 3) 。 Moisture to dry the basic empty bearing ring into the oven inside 60 degrees / 10 minutes to adjust to 110 degrees for 10 minutes; Remove after the generation of high temperature of bearing ring easy to rust, processing methods: quickly into the sealed bucket, pour while injection point (anhydrous ethanol Industrial alcohol) Pour into a circle, a thin layer of alcohol ( Do not spray too much) , will be sealed lid seal, bearing ring is stored in a sealed bucket after cold. An airtight storage barrel is mainly to prevent rust. What are removed to paint coating, coating yon take while coated with or immersed in coating or spray paint. Bearing ring as long as the glue coated with adhesive solution will not rust, take after sealing lid in time, to minimize the bearing ring in contact with air. Reports from local environment humidity condition or sealing conditions can save - 3 days 6 days not rust. Basic principle: the use of low surface energy resin dip the nano material bearing play for quench, stamping and produce a crack and crack phosphating film on the surface of microporous or gap, fully filled only under a microscope you can see the bearing surface of the 'gap', the purpose of anticorrosive wear-resisting performance. When bearing surface treatment technology, generally USES the bearing of working face in the generation of functional nano materials, in the rust/corrosion/wear resistance ( Extend your life) / low friction coefficient, high temperature resistant/thermal expansion contradiction balance processing precision and gap/comprehensive performance greatly improve the quality and conflicting indicators such as received, offers an excellent balance. This process is one of the most key technology of the bearing quality.